PEACOCK BLUE MATTE

My original #507-15 glaze from my first glaze class, a dependable semi matte glaze that makes a variety of intense turquoise blue colors depending on the percentage of chromium oxide or cobalt carbonate added.

Peacock Blue Matte

Custer Felspar                    400
Nepheline Syenite A-270    120
Dolomite                             75
Barium Carbonate              160
EPK                                  135
Silica                                 110

Add .4% cobalt carbonate and .6% chromium oxide.

750 ml water.

COPPER GREY

A semi-matte glaze that usually fires a solid pewter grey without much difference between clay bodies.

Occasionally flashes reds and pinks.

Copper Grey Recipe

Feldspar-G200 HP          263
Frit-ferro 3195-2             118
Dolomite                        113
Talc                               132
Ball Clay- Old Mine #4     91
Silica                             283

Add  6g copper carbonate.

VICTORIA'S CREAM

I got this recipe from Victoria Morris.
A creamy matte buttermilk that turns much whiter on the second dip. It has a great smooth texture and varies greatly depending on the clay body.
High in Barium, and turns much more yellow in the presence of iron.

This glaze is extremely matte and will stain with a marker - probably not a good choice for dinnerware.

Victoria's Cream Recipe

Nepheline Syenite A-270        470
Dolomite                               171
Barium Carbonate                  171
EPK                                       60
Zircopax plus                        128
.5% yellow iron oxide

*adding
up to 2% yellow iron oxide will make a pretty yellow

750 ml H2O

GLOSSY GLAZE 709-27

This was Sandy's glaze and made several nice colors with the addition of iron and nickel,  and an incredibly reactive vanadium glaze I am calling "Starry Night".


Nickel made a nice grey-brown, especially at Ni-1(.4%) and Ni-2 (.8%):

Starry Night was best around 2-3% vanadium.

 Fe-2, Fe3 and Fe4 all made pretty blue greens.

709-27 Recipe

Feldspar - minspar 250      370

Whiting                            160

Dolomite                             20

Kaolin-Grolleg                  150

Imsil Silica                        300

750 ml H2O

Ni-1                   .4% nickel

Ni-2                   .8% nickel

Vanadium           2-3% vanadium

Fe-2,3,4              2-4% red iron oxide

GLOSSY GLAZE 705-15

This was Loren's glaze and he had several nice results from his triaxial blend.

D: a nice honey amber color
G: a tobacco brown
K: looked like coca cola, with bits of blue in it.
M: looked like blue smoke
P: a gorgeous deep plum with lots of variation
R:  a dark smokey grey.

RECIPE 705-15

NC-4 Feldspar                        464

Talc                                        46

Wollastonite NYAD M200      102

Zinc Oxide 506                        18

Bentonite                                 30

Grolleg Kaolin                          81

Silica                                      167

Tin Oxide                                 46

G-Zircon Milled F                     46

H2O: 900 ml

D:   12g red iron oxide 

      16g rutile

G:   8 g red iron oxide

       24g rutile

K:   4g red iron oxide

       32g rutile

M:  4g red iron oxide

      16g rutile

       2.4g cobalt oxide

P:  40g rutile

R:  24g rutile

      2.4g cobalt oxide

HARE'S FUR GLAZE

I hope this one works! I tried the Nuka recipe.

Tested on several clay bodies.

RESULTS:
I tried the "Nuka" recipe.
This didn't turn out at all like the image above, but it is a nice matte white glaze - very clean white with good coverage.
Here it is on Babu, granite, soldate, and black mountain:

*Ok what I realized is that you have to use BOTH glazes together!

GLOSSY GLAZE 905-6

Glaze 905-6

A glossy glaze with a slight crackle.  Has some magnesium in it.

Custer Feldspar                           392

Wollastonite NYAD M200        161

Talc                                            42

Grolleg Kaolin                            59

Old Mine #4                               87

Silica                                         259                  Total 1000

H₂O:  700 ml

Rogers note:
"This one is similar to 1108-30 but with a bit of magnesium.  Probably would be a good testing base, but the W-30 wollastonite might make it a bit hard to screen."

RESULTS:

My glaze didn't have any crazing.

Added praseodymium yellow at 8% 4% 2% and 1%

Very pale sherbet green colors.

At 8% The glaze needed more water - you can see that it crawled.

Lavender stain at 8%,4%, 2%, and 1%

 

Additionally added some neodymium to the  4% Lavender, and tested a tile that was a "mix" of all the percentages.

Seems to be stable and reliable, but also a bit boring glaze without much depth.
I should test it on some other clay bodies.